Product Details

Variolink N is suitable for the cementation of indirect restorations made of leucite-reinforced glass-ceramics (IPS Empress), lithium disilicate glass

3M ESPE RelyX Luting 2 Refill Pack (1 Cartridge) 1 – 11 g RelyX™ Luting 2 Cement in Clicker™ Dispenser

Pack Size : 1 – 11 g RelyX™ Luting 2 Cement in Clicker™ Dispenser

Request a Quote

RelyX Luting 2 by 3M is an advanced, self-curing, radiopaque, fluoride releasing resin-modified glass ionomer luting cement. The RMGI luting cement comes in a paste-paste delivery system from the ‘Clicker’. RelyX exhibits high bond strength and virtually no post-operative sensitivity. A low film thickness ensures a perfect fit for all indirect restorations. It also exhibits strong adhesive properties and enhanced marginal integrity. Once the procedure is completed, the excess cement can be easily removed. RelyX has low solubility and prevents the wash-out of the luting cement under indirect restorations. The fluoride release is higher than the conventional glass ionomer cements. The use of RelyX for luting indirect restorations ensures optimum results.

 

Warning: RelyX Luting 2 contains acrylate resins such as HEMA and is contraindicated in allergic patients. 

 

 Easy and hygienic handling - Clicker Dispenser
 Low film thickness - for perfect indirect restorations
 
 
 Strong adhesion, enhanced marginal integrity
 Easy removal of excess material
 

Storage: 

Store RelyX Luting 2 at room temperature of 21-24°C.                       

The shelf life of the cement once the foil pouch is opened is 6 months. Refrigeration of the product can extend shelf life. The material should be allowed to come to room temperature before use

 

  • The double barrel ‘Clicker’ dispenser allows hygienic and fast delivery of the cement in a required quantity and consistent mix ratio
  • Click and mix the cement directly from the ‘Clicker’ onto the mixing pad
  • Simple dosing and easy paste-paste mixing ensure consistent material properties.
  • 2 clicks of the material are recommended for a single crown
  • Based on the above recommendation, 40 single unit crowns can be seated using the RelyX Luting 2 in the Clicker dispenser
  • A total of 80 clicks are available in a single Clicker dispenser.

 

5 simple steps: 

  • DELIVER the cement onto the mixing pad
  • MIX the delivered quantity of cement
  • LOAD the indirect restoration with the mixed cement
  • SEAT the indirect restoration in place
  • REMOVE the excess cement after the material has set.      

 

Working time of mixed cement

2.5 minutes

Set time after placement in the mouth

5 minutes

 

Tech Specs

RelyX Luting 2 Cement

Compressive strength (MPa)

160.0 ± 8.8

Flexural Strength (MPa)

31.6 ± 4.1

Diametral Tensile Strength (MPa)

25.5 ± 2.3

Shear adhesion to enamel (MPa)

10.3 + 1.8

Shear adhesion to dentin (MPa)

5.7 + 1.8

Shear adhesion to metal (MPa)

10.5 + 2.6

Shear adhesion to zirconia (MPa)

9.2 + 2.5

Shear adhesion to alumina (MPa)

14.2 + 1.9

Shear adhesion to amalgam core build-up (MPa)

8.7 + 2.7

Shear adhesion to composite resin core build-up (MPa)

5.3 + 2.1

Shear adhesion to GIC core build-up (MPa)

6.7 + 1.9

Radiopacity (mm)

1.42 ± 0.01

Film Thickness (microns)

15.3 ± 1.5

 

3M RelyX luting cement can be used in cementation of: 

  • Metal crowns, inlays and onlays
  • PFM crowns and bridges
  • All-ceramic crowns such as all-zirconia or all-alumina ceramic restorations
  • Endodontic pins and posts
  • Orthodontic appliances
  • PFM, Metal, Alumina or All-Alumina core restorations on implant abutments
  • Better shear strength
  • Excess cement can be removed within seconds
  • Sustained fluoride release
  • Improved clinical performance
  • Easy & hygienic handling
  • Low film thickness ensures perfect fit
  • Strong adhesion
  • Low solubility and enhanced marginal integrity
  • Easy removal of excess cement
  • Low post-operative sensitivity
  • White shade